Ibrahim, R. and Azmirruddin, M. and Jabir, M. and Ridhuan, M. and Muhamad, M. and Rafiq, M. and Abu Kasim, N.H. and Muhamad, S. (2010) Development of craniofacial implants produced by metal injection molding of titanium alloy using novel binder system based on palm oil. Advances in Science and Technology, 76. pp. 247-252. ISSN 3908158591

[img]
Preview
PDF
Download (27Kb) | Preview

    Abstract

    Metal Injection Molding (MIM) is a cost-effective technique for producing small, complex, precision parts in high volumes. MIM consists of four main processing steps: mixing, injection molding, debinding and sintering. In the mixing step, the powder titanium alloy (Ti6Al4V) medical grade is mixed with a binder system based on palm stearin to form a homogeneous feedstock. The rheological studies of the feedstock have been determined properly in order to success during injection into injection molding machine. After molding, the binder holds the particles in place. The binder systems then have to be removed completely through debinding step. Any contamination of the binder systems will affect the final properties of the parts. During debinding step, solvent extraction debinding has been used to remove partly of the binder systems. The debound part is then sintered at high temperature under control atmosphere furnace. The properties of the sintered craniofacial implants then was measured and compared. The sintered craniofacial implants also then were determined in term of in-vitro cytotoxicity study using mouse fibroblast lines L-929. The results show that the sintered craniofacial implants of titanium alloy produced by MIM fullfill the in-vitro cytotoxicity test.

    Item Type: Article
    Additional Information: Associate Prof. Dr. Noor Hayaty Binti Abu Kasim Department of Conservative Dentistry, Faculty of Dentistry, University of Malaya, 50603 Kuala Lumpur, MALAYSIA
    Uncontrolled Keywords: In Vitro Cytotoxicity Test; Binder System; Debinding; Sintering; Solvent Extraction; Self-Repair; Culture-Conditions; Composite Resin; Dental Pulp Stem Cell; Functionally Graded Design; Multi Layered Post; Functionally Graded Dental Post; Soft Skills; Clinical Pairing; Dental Pulp Stromal Cells; Long-Term Expansion
    Subjects: Medicine and Dentistry
    Medicine and Dentistry > Clinical Medicine
    Medicine and Dentistry > Clinical Dentistry
    Divisions: UNSPECIFIED
    Depositing User: Associate Prof. Dr. Noor Hayaty Abu Kasim
    Date Deposited: 13 Feb 2012 01:15
    Last Modified: 13 Feb 2012 01:15
    URI: http://opendepot.org/id/eprint/710

    Actions (login required)

    View Item